Feeding mechanisms in high-pressure die castings

This work focuses on understanding the feeding behavior during high-pressure die casting (HPDC). The effects of intensification pressure (IP) and gate thickness on the transport of material through the gate during the latter stages of HPDC were investigated using an Al-Si3MgMn alloy. Microstructural characterization of the gate region indicated a marked change in feeding mechanism with increasing IP and gate size. Castings produced with a high IP or thick gate contained a relatively low fraction of total porosity, and shear band-like features existed through the gate, suggesting that semisolid strain localization in the gate is involved in feeding during the pressure intensification stage. When a low IP is combined with a thin gate, no shear band is observed in the gate and feeding is less effective, resulting in a higher level of porosity in the HPDC component. Although shear banding through the gate was found to reduce porosity in HPDC parts, if gates are not properly designed, deformation of the mushy zone through the gate can cause severe macrosegregation, large pores, and large cracks, which could severely reduce the performance of the component