Atomic Imaging of the Irreversible Sensing Mechanism of NO₂ Adsorption on Copper Phthalocyanine

Ambient NO₂ adsorption onto copper­(II) phthalocyanine (CuPc) monolayers is observed using ultrahigh vacuum (UHV) scanning tunneling microscopy (STM) to elucidate the molecular sensing mechanism in CuPc chemical vapor sensors. For low doses (1 ppm for 5 min) of NO₂ at ambient temperatures, isolated chemisorption sites on the CuPc metal centers are observed in STM images. These chemisorbates almost completely desorb from the CuPc monolayer after annealing at 100 °C for 30 min. Conversely, for high NO₂ doses (10 ppm for 5 min), the NO₂ induces a fracture of the CuPc domains. This domain fracture can only be reversed by annealing above 150 °C, which is consistent with dissociative chemisorption into NO and atomic O accompanied by surface restructuring. This high stability implies that the domain fracture results from tightly bound adsorbates, such as atomic O. Existence of atomic O on or under the CuPc layer, which results in domain fracture, is revealed by XPS analysis and ozone-dosing experiments. The observed CuPc domain fracturing is consistent with a mechanism for the dosimetric sensing of NO₂ and other reactive gases by CuPc organic thin film transistors (OTFTs)