Self-Organization of Nanorods into Ultra-Long Range Two-Dimensional Monolayer End-to-End Network

Highly uniform large-scale assembly of nanoscale building blocks can enable unique collective properties for practical electronic and photonic devices. We present a two-dimensional (2-D), millimeter-scale network of colloidal CdSe nanorods (NRs) in monolayer thickness through end-to-end linking. The colloidal CdSe NRs are sterically stabilized with tetradecylphosphonic acid (TDPA), and their tips are partially etched in the presence of gold chloride (AuCl₃) and didecyldimethylammonium bromide (DDAB), which make them unwetted in toluene. This change in surface wetting property leads to spontaneous adsorption at the 2-D air/toluene interface. Anisotropy in both the geometry and the surface property of the CdSe NRs causes deformation of the NR/toluene/air interface, which derives capillary attraction between tips of neighboring NRs inward. As a result, the NRs confined at the interface spontaneously form a 2-D network composed of end-to-end linkages. We employ a vertical-deposition approach to maintain a consistent rate of NR supply to the interface during the assembly. The rate control turns out to be pivotal in the preparation of a highly uniform large scale 2-D network without aggregation. In addition, unprecedented control of the NR density in the network was possible by adjusting either the lift-up speed of the immersed substrate or the relative concentration of AuCl₃ to DDAB. Our findings provide important design criteria for 2-D assembly of anisotropic nanobuilding blocks