Visoelastic studies on thermoplastic polyurethane nanocomposites using a nano-hardness tester

The viscoelastic behaviour of a range of polyurethane thermoplastic elastomer montmorillonite nanocomposites has been studied using a nanohardness tester. For softer Shore hardness 80A materials, the introduction of the organo-clay increased the creep strain obtained while the nano-indentor was held at constant load. The increase in creep strain was greatest for materials containing an organo-clay modified with a more hydrophilic quaternary alkylammonium surfactant and with higher loadings of the hydrophilic organo-clay. This suggested the effect might be due to a plasticising effect of the excess surfactant. For the harder Shore hardness 55D materials, the addition of the organo-clays produced only a small decrease in the creep strain, probably due to the interconnected hard domains in this material