Synergistic Effects of Gold–Palladium Nanoalloys and Reducible Supports on the Catalytic Reduction of 4‑Nitrophenol

Herein we report on the catalytic activity of mesoporous nickel, iron, cerium, cobalt, and manganese oxides prepared using KIT-6 as a hard template via evaporation-assisted precipitation. The mesoporous metal oxides (MMOs) were characterized and used as heterogeneous catalysts in the reduction of 4-nitrophenol (4-Nip) by sodium borohydride (BH₄^–). Furthermore, polyamidoamide (PAMAM) dendrimers were used to synthesize gold–palladium nanoalloy particles. The size of AuPd/PAMAM was found to be 3.5 ± 0.8 nm in diameter before being immobilized on the aforementioned mesoporous metal oxides and used as catalysts in the reduction of 4-Nip. Prior to catalytic evaluation, the reduction profiles of the mesoporous metal oxides were investigated by hydrogen-temperature-programmed reduction (H₂-TPR) and showed that mesoporous metal oxides can be easily reduced at lower temperatures and that the immobilization of gold–palladium nanoalloy particles lowers their reduction temperatures. Mesoporous cobalt and manganese oxides showed catalytic activity toward 4-Nip reduction, and the activity was enhanced after immobilization of the gold–palladium nanoalloys. Isolation of nanoparticles activity was achieved by immobilization of the gold–palladium nanoalloys on the inert silica support. From this we postulated an electron relay mechanism for the reduction of 4-nitrophenol. With the use of power rate law we showed that 4-Nip reduction follows pseudo-first-order kinetics