Micro-Fracture Toughness in a Nanoceramic Composite

Micro-fracture toughness in one nanoceramic composite, Al_2O_3/SiC_{nano}, is measured by Nanoindentation tests. Microscopy is adopted to probe that all nanoindentations are local at Al_2O_3, matrix component of the current composite and measure length of radial micro-cracks at corriers of nanoindentation. The measured fracture toughness at the shallow indentation is higher than those at deeper ones. Relations between micro-toughness and peak loads as well as peak depths are discussed. And an analysis to the energy consumed during the indentation and fracture toughness explained that, the lower fracture toughness measured in the deeper impression probably resulted from its fracture modes yielded by higher load and larger depth