Add to ORKGEffects of aging on several dental composites were studied using a torsion creep apparatus. A constant torque was applied from 1 second to 3 hours, and recovery was observed from 10 seconds to 2 days, for specimens aged from 3 hours to 8 weeks following polymerization. Specimens aged for shorter times exhibited more creep and less complete recovery than specimens aged for longer times. Modulus and creep results were qualitatively consistent with a composite model for particulate inclusions.X116sciescopu
Objectives: The aim of this study was to develop a method for measuring the slumping resistance of r...
1. Objective: Over time dental composites age due to mechanical impacts such as chewing and chemical...
International audienceAbstract While dental composite long-term aging has already been studied in th...
The viscoelastic properties of three commercially available resin-based composites (Filtek™ P60, Fil...
The viscoelastic properties of three commercially available resin-based composites (Filtek™ P60, Fil...
Dental composite materials (CM) are widely used in dentistry for restorations. The aim of this study...
Over time dental composites age due to mechanical impacts such as chewing and chemical impacts such ...
Aim. The purpose of this in vitro study was to determine the effect of thermally accelerated aging o...
The aim of this study is to compare the creep/recovery behavior of bulk-fill dental composites after...
Aim: The purpose of this study was to evaluate the Vicker's hardness and surface roughness of eight ...
The mandible from the structural mechanics point of view at the macroscopic level is a highly comple...
While many publications concentrate on the characterization of the mechanical and physical propertie...
Physical aging studies near the conventional glass transition temperature Tg were made using a model...
Surface morphology and wear characteristics of five dental composites subjected to accelerated aging...
An experimental study was undertaken to establish the viscoelastic behavior of 1M7/K3B composite in ...
Objectives: The aim of this study was to develop a method for measuring the slumping resistance of r...
1. Objective: Over time dental composites age due to mechanical impacts such as chewing and chemical...
International audienceAbstract While dental composite long-term aging has already been studied in th...
The viscoelastic properties of three commercially available resin-based composites (Filtek™ P60, Fil...
The viscoelastic properties of three commercially available resin-based composites (Filtek™ P60, Fil...
Dental composite materials (CM) are widely used in dentistry for restorations. The aim of this study...
Over time dental composites age due to mechanical impacts such as chewing and chemical impacts such ...
Aim. The purpose of this in vitro study was to determine the effect of thermally accelerated aging o...
The aim of this study is to compare the creep/recovery behavior of bulk-fill dental composites after...
Aim: The purpose of this study was to evaluate the Vicker's hardness and surface roughness of eight ...
The mandible from the structural mechanics point of view at the macroscopic level is a highly comple...
While many publications concentrate on the characterization of the mechanical and physical propertie...
Physical aging studies near the conventional glass transition temperature Tg were made using a model...
Surface morphology and wear characteristics of five dental composites subjected to accelerated aging...
An experimental study was undertaken to establish the viscoelastic behavior of 1M7/K3B composite in ...
Objectives: The aim of this study was to develop a method for measuring the slumping resistance of r...
1. Objective: Over time dental composites age due to mechanical impacts such as chewing and chemical...
International audienceAbstract While dental composite long-term aging has already been studied in th...