The thesis study the effects of corrosion on the mechanical characteristics of steel rebars and consequently on the performance of reinforced concrete elements with particular attention to fatigue and ductility. The thesis also investigate the relation between the intensity of the anodic current used in durability tests to activate rebar corrosion and the morphology of the induced corrosion damage. The problem was experimentally investigated by comparing the mechanical characteristics of noncorroded and laboratory corroded rebars
Corrosion of reinforcement is a common form of degradation of reinforced concrete structures. The ch...
Trabajo presentado en el 8th International Conference on Fracture Mechanics of Concrete and Concrete...
In this work 144 reinforcing bars of high-ductility steel named B500SD were subjected to an accelera...
Corrosion of steel reinforcement is one of the most severe problems of durability in reinforced conc...
Corrosion of steel reinforcement is one of the most severe problems of durability in reinforced conc...
Corrosion of steel reinforcement is one of the most severe problems of durability in reinforced conc...
Corrosion can be a major concern in term of durability and the safety of the reinforced concrete str...
Reinforcement corrosion in concrete is regarded as the predominant factor in the premature degradati...
Corrosion of the reinforcement is a common form of degradation of reinforced concrete structures. A...
Corrosion of reinforcement is a common form of degradation of reinforced concrete structures. The ch...
Corrosion of reinforcement is a common form of degradation of reinforced concrete structures. The ch...
Reinforced concrete has been a widely used construction material due to its strength and versatility...
Corrosion of reinforcement is a common form of degradation of reinforced concrete structures. The ch...
Corrosion of the reinforcement is a common form of degradation of reinforced concrete structures. A...
Corrosion of reinforcement is a common form of degradation of reinforced concrete structures. The ch...
Corrosion of reinforcement is a common form of degradation of reinforced concrete structures. The ch...
Trabajo presentado en el 8th International Conference on Fracture Mechanics of Concrete and Concrete...
In this work 144 reinforcing bars of high-ductility steel named B500SD were subjected to an accelera...
Corrosion of steel reinforcement is one of the most severe problems of durability in reinforced conc...
Corrosion of steel reinforcement is one of the most severe problems of durability in reinforced conc...
Corrosion of steel reinforcement is one of the most severe problems of durability in reinforced conc...
Corrosion can be a major concern in term of durability and the safety of the reinforced concrete str...
Reinforcement corrosion in concrete is regarded as the predominant factor in the premature degradati...
Corrosion of the reinforcement is a common form of degradation of reinforced concrete structures. A...
Corrosion of reinforcement is a common form of degradation of reinforced concrete structures. The ch...
Corrosion of reinforcement is a common form of degradation of reinforced concrete structures. The ch...
Reinforced concrete has been a widely used construction material due to its strength and versatility...
Corrosion of reinforcement is a common form of degradation of reinforced concrete structures. The ch...
Corrosion of the reinforcement is a common form of degradation of reinforced concrete structures. A...
Corrosion of reinforcement is a common form of degradation of reinforced concrete structures. The ch...
Corrosion of reinforcement is a common form of degradation of reinforced concrete structures. The ch...
Trabajo presentado en el 8th International Conference on Fracture Mechanics of Concrete and Concrete...
In this work 144 reinforcing bars of high-ductility steel named B500SD were subjected to an accelera...
Add to ORKG