Temperature stable K0.5(Nd1−xBix)0.5MoO4 microwave dielectrics ceramics with ultra-low sintering temperature

K 0.5 (Nd 1-x Bi x ) 0.5 MoO 4 (0.2 ≤ x ≤ 0.7) ceramics were prepared via the solid-state reaction method. All ceramics densified below 720°C with a uniform microstructure. As x increased from 0.2 to 0.7, relative permittivity (e(open) r ) increased from 13.6 to 26.2 commensurate with an increase in temperature coefficient of resonant frequency (TCF) from - 31 ppm/°C to + 60 ppm/°C and a decrease in Qf value (Q = quality factor; f = resonant frequency) from 23 400 to 8620 GHz. Optimum TCF was obtained for x = 0.3 (-15 ppm/°C) and 0.4 (+4 ppm/°C) sintered at 660 and 620°C with e(open) r ~15.4, Q f ~19 650 GHz, and e(open) r ~17.3, Q f ~13 050 GHz, respectively. Ceramics in this novel solid solution are a candidate for ultra low temperature co-fired ceramic (ULTCC) technology