Ponovljivost ispitivanja svojstava apsorpcije energije Aluminijske pjene

Aluminium foam is, principally, a composite material consisting of aluminium or aluminium alloy matrix and of pores filled up with a gas distributed throughout the matrix. This paper studies the reproducibility of aluminium foams energy absorption properties. Samples of aluminium foam were produced from an Alulight precursor (AlMgSi0.6 TiH2-0.4). This precursor was placed into a mould form and heated up until the agent starts to foam. Immediately thereafter the mould is taken out of the furnace and cooled off, so the aluminium foam part is frozen in shape. The ability of samples to absorb mechanical energy was estimated from the results of compression tests. Test results showed that aluminium foams have good energy absorption properties and reproducibility is relatively low.Aluminijska pjena je u osnovi kompozitni materijal koji se sastoji od aluminijske osnove ili osnove od neke aluminijske legure i pora ispunjenih plinom. Ovaj rad istražuje ponovljivost rezultata ispitivanja svojstava apsorpcije energije aluminijske pjene. Uzorci aluminijske pjene proizvedeni su iz “Alulight” prekursora (AlMgSi 0.6 TiH2-0.4). Prekursor je stavljen u kalup i zagrijavan sve dok se plinski agens nije počeo pjeniti. Nakon toga je kalup izvađen iz peći i hlađen pri čemu je uzorak pjene poprimio oblik kalupa. Iskoristivost apsorpcije energije aluminijskih pjena procjenjena je iz rezultata tlačnog ispitivanja. Rezultati ispitivanja pokazali su da aluminijske pjene imaju dobra svojstva apsorpcije energije i da je ponovljivost rezultata relativno niska