Erozija nodularnog lijeva česticama kvarcnog pijeska

Ductile cast iron has high fatigue strength due to the spherical shape of graphite, especially after quenching and tempering. Higher toughness can be achieved by austempering. One of the advantages of ductile cast iron in relation to other cast irons is its good wear resistance. In the experiments, samples of ductile cast iron and austempered ductile cast iron were eroded with quartz sand particles at six different angles of impact (15°, 30°, 45°, 60°, 75° and 90°). The test results were presented as the loss of mass which occured during the test. Testing with quartz sand shows that the particle erosion resistance of ductile cast iron was better than that of austempered ductile iron for all impact angles except for 60°. The maximum measured wears of ductile cast iron and austempered ductile iron were at 75°.Nodularni lijev ima veliku dinamičku izdržljivost zbog kuglastog oblika grafita, naročito nakon poboljšavanja. Visoka žilavost može se postići izotermičkim poboljšavanjem. Jedna od prednosti nodularnog lijeva u odnosu na ostale željezne lijevove je njegova dobra otpornost na trošenje. U ovom istraživanju ispitivana je otpornost na erozijsko trošenje nodularnog lijeva i izotermički poboljšanog nodularnog lijeva, česticama kvarcnog pijeska pri šest različitih kutova udara (15°, 30°, 45°, 60°, 75° and 90°). Rezultati ispitivanja prikazani su gubitkom mase tijekom ispitivanja. Rezultati pokazuju da nodularni lijev ima bolju otpornost na erozijsko trošenje od izotermički poboljšanog nodularnog lijeva pri svim kutovima udara osim kod 60°. Maksimalni gubitak mase kod oba materijala zabilježen je pri kutu upada od 75°