Fatigue life prediction and strength degradation of wind turbine rotor blade composites

Wind turbine rotor blades are subjected to a large number of highly variable loads, but life predictions are typically based on constant amplitude fatigue behaviour. Therefore, it is important to determine how service life under variable amplitude fatigue can be estimated from constant amplitude fatigue behaviour. A life prediction contains different, partly independent, elements: · the counting method, used for describing variable amplitude signals as a collection of constant amplitude cycles · formulations for describing S-N curves which relate the stresses to the number of cycles to failure · constant life diagrams which are made up of S-N curves for different stress ratios · damage rules, which relate the life expectancy of a specimen to the stress history For the description of damage, two models were investigated and compared, viz. the Miner's sum method and strength-based life prediction. In the Miner's sum method, the results of a counting method and constant amplitude fatigue behaviour description are converted into a damage parameter, "Miner's sum". Potential effects of load order are not taken into account. Moreover, the value of the damage parameter only indicates whether or not failure occurred: it does not relate to a physically quantifiable damage. These are limitations to the model which suspectedly might cause inaccurate predictions. In the strength-based method, life is predicted by calculating the effect of each load cycle on strength, until the load exceeds the remaining strength. An expected advantage of this cycle-by-cycle method is, that sequence effects can be implicitly included. Moreover, the damage parameter is at all times related to a physically quantifiable parameter (viz. strength). The successful application of the strength-based method requires a description of the post-fatigue strength, which entails considerable experimental effort. In addition, a strength-based life prediction is much more computationally intensive than Miner's sum and can not always utilise the same counting methods. In the comparison of the Miner's sum and the strength-based method, the influence and significance of the other life prediction elements, such as counting methods and description of constant amplitude fatigue behaviour on life prediction are included. The experimental research involved a considerable amount of material tests. The material tests give a detailed image of static strength, constant and variable amplitude fatigue behaviour (both block tests and (variants of) the WISPER spectrum were used), as well as strength degradation for different glass-fibre reinforced laminates. By selecting a single coupon geometry for all material tests on a single material, and the definition and use of standard test conditions, a consistent database was created. The block-test experiments confirm the existence of sequence effects on life, although more data are required to fully quantify them. The residual strength tests show the strength degradation after fatigue for a range of fatigue load conditions. Significant tensile strength degradation is observed in R=0.1 and R=-1 fatigue experiments. Generally, compressive strength remains within the boundaries of the initial static strength distribution. This behaviour was observed for different laminates. The significance of an adequate description of the constant amplitude behaviour is evident from the various life predictions. Commonly used simplifications, such as the Linear Goodman Diagram, result in highly non-conservative predictions. The residual strength model yields more conservative predictions than Miner's sum for the investigated tension-dominated load sequences. The experimental effort required for the determination of the strength degradation, and the computational effort do not justify this relatively small advantage. For future research, it is recommended to further improve the description of the constant life diagram. This work is focussed on fatigue of composites for wind turbine rotor blades. Nevertheless, the results are relevant for other composite structures as well.Aerospace Engineerin