Add to ORKGThe present investigation aims to inquire whether Al cladding of 2024 aluminum alloy specimens could provide, additionally to the expected protection against corrosion damage, also a protection against the corrosion induced hydrogen embrittlement of the alloy. The latter is observed when bare 2024 material is subjected to laboratory exfoliation corrosion exposure in the absence of mechanical loading. The study aims also to ponder on the question whether local Al cladding at small regions of the specimen surface might suffice for protecting the specimen against corrosion damage and hydrogen embrittlement. The work comprises the results of an extensive experimental investigation including tensile tests on precorroded 2024 specimens protected ...
Aluminium is an interesting material for use in subsea applications due to the combination of low we...
The study investigates the effect of prior corrosive exposure on crack growth resistance behaviour o...
A multi-scale modeling approach for simulating the tensile behavior of the corroded aluminum alloy 2...
The present investigation aims to inquire whether At cladding of 2024 aluminum alloy specimens could...
Corrosion is a major concern to the structural integrity of aging aircraft structures. The effect of...
Corrosion is a major concern to the structural integrity of aging aircraft structures. The effect of...
The present paper focuses on the observed corrosion-induced embrittlement of alloy 2024 and tries to...
Exfoliation and alternate immersion corrosion were investigated in Al alloy 2024-T3 (UNS A92024) upt...
International audienceTo study the influence of hydrogen on the intergranular corrosion mechanism of...
High-pressure hydrogen tanks which are composed of an aluminum alloy liner and a carbon fiber wound ...
It is more difficult with aluminum alloys to investigate the effect of hydrogen on their mechanical ...
The paper reports the results of research on the effect of hydrogen penetration on the variations in...
AbstractIn the present work, the effect of artificial ageing of AA2024-T3 on the tensile mechanical ...
Stress corrosion and corrosion fatigue represent major threats to the structural integrity of aircra...
In the framework of a collaborative program research with EADS Innovation Works and AIRBUS, this wor...
Aluminium is an interesting material for use in subsea applications due to the combination of low we...
The study investigates the effect of prior corrosive exposure on crack growth resistance behaviour o...
A multi-scale modeling approach for simulating the tensile behavior of the corroded aluminum alloy 2...
The present investigation aims to inquire whether At cladding of 2024 aluminum alloy specimens could...
Corrosion is a major concern to the structural integrity of aging aircraft structures. The effect of...
Corrosion is a major concern to the structural integrity of aging aircraft structures. The effect of...
The present paper focuses on the observed corrosion-induced embrittlement of alloy 2024 and tries to...
Exfoliation and alternate immersion corrosion were investigated in Al alloy 2024-T3 (UNS A92024) upt...
International audienceTo study the influence of hydrogen on the intergranular corrosion mechanism of...
High-pressure hydrogen tanks which are composed of an aluminum alloy liner and a carbon fiber wound ...
It is more difficult with aluminum alloys to investigate the effect of hydrogen on their mechanical ...
The paper reports the results of research on the effect of hydrogen penetration on the variations in...
AbstractIn the present work, the effect of artificial ageing of AA2024-T3 on the tensile mechanical ...
Stress corrosion and corrosion fatigue represent major threats to the structural integrity of aircra...
In the framework of a collaborative program research with EADS Innovation Works and AIRBUS, this wor...
Aluminium is an interesting material for use in subsea applications due to the combination of low we...
The study investigates the effect of prior corrosive exposure on crack growth resistance behaviour o...
A multi-scale modeling approach for simulating the tensile behavior of the corroded aluminum alloy 2...