Oxidation behavior and microstructural evolution of Ti-6Al-4V and Ti-6Al-4V-1B sheet

A direct comparison between the oxidation behavior of Ti-6Al-4V and Ti-6Al-4V + 1B has been conducted to elucidate whether the addition of boron to Ti-6Al-4V impacts the oxidation behavior. Industrially prepared sheet of Ti-6Al-4V and Ti-6Al-4V + 1B were oxidized at temperatures between 650 and 950 °C for holding times of 25 and 50 h. Weight-gain measurements and characterization of surface and near-surface microstructures showed that the addition of 1 wt% B increased the material’s oxidation resistance. Additionally, the ingress of oxygen tends to decrease the solubility of other alloying species in α-Ti and leads to the formation of a distinctive and atypical microstructure with a distinct morphology