Add to ORKGThe aim of this research was to understand the Stress Corrosion Cracking (SCC) of rock bolts. The laboratory tests have produced fracture surfaces similar to those from service. The experimental study elucidated the environmental condition leading to rock bolt SCC, and was used to determine the threshold stress and the threshold potential. A hydrogen embrittlement mechanism is proposed.Erwin Gamboa, Ernesto Villalba and Andrej Atren
in order to understand the metallurgical influences on rock bolt stress corrosion cracking (SCC), an...
A new laboratory facility designed and constructed at the University of New South Wales, aims to con...
Premature failure of rockbolts from stress corrosion cracking (SCC) has been a problem in a limited ...
The aim of this research was to understand the Stress Corrosion Cracking (SCC) of rock bolts. The la...
The aim of this research was to understand the Stress Corrosion Cracking (SCC) of rock bolts. The la...
The aim of this research was to understand the Stress Corrosion Cracking (SCC) of rock bolts. The la...
ABSTRACT: The aim of this research was to understand the Stress Corrosion Cracking (SCC) of rock bol...
Copyright © 2003 Elsevier Ltd. All rights reserved.In order to understand rock bolt Stress Corrosion...
Copyright © 2004 Elsevier Ltd All rights reserved.Rock bolt stress corrosion cracking (SCC) has been...
ABSTRACT: The incidence of Stress Corrosion Cracking (SCC) in rock bolts has not been quantified an...
Rock bolts have failed by Stress Corrosion Cracking (SCC). This paper presents a detailed examinatio...
The influence of steel metallurgy on rock bolt SCC was studied using a series of commercial carbon a...
The stress corrosion cracking of rock bolts has been explored using Linearly Increasing Stress Tests...
The work describes a study of stress corrosion cracking (SCC) failure of rock bolts in underground c...
This paper considers our recent research on rock bolt stress corrosion cracking (SCC) which studied ...
in order to understand the metallurgical influences on rock bolt stress corrosion cracking (SCC), an...
A new laboratory facility designed and constructed at the University of New South Wales, aims to con...
Premature failure of rockbolts from stress corrosion cracking (SCC) has been a problem in a limited ...
The aim of this research was to understand the Stress Corrosion Cracking (SCC) of rock bolts. The la...
The aim of this research was to understand the Stress Corrosion Cracking (SCC) of rock bolts. The la...
The aim of this research was to understand the Stress Corrosion Cracking (SCC) of rock bolts. The la...
ABSTRACT: The aim of this research was to understand the Stress Corrosion Cracking (SCC) of rock bol...
Copyright © 2003 Elsevier Ltd. All rights reserved.In order to understand rock bolt Stress Corrosion...
Copyright © 2004 Elsevier Ltd All rights reserved.Rock bolt stress corrosion cracking (SCC) has been...
ABSTRACT: The incidence of Stress Corrosion Cracking (SCC) in rock bolts has not been quantified an...
Rock bolts have failed by Stress Corrosion Cracking (SCC). This paper presents a detailed examinatio...
The influence of steel metallurgy on rock bolt SCC was studied using a series of commercial carbon a...
The stress corrosion cracking of rock bolts has been explored using Linearly Increasing Stress Tests...
The work describes a study of stress corrosion cracking (SCC) failure of rock bolts in underground c...
This paper considers our recent research on rock bolt stress corrosion cracking (SCC) which studied ...
in order to understand the metallurgical influences on rock bolt stress corrosion cracking (SCC), an...
A new laboratory facility designed and constructed at the University of New South Wales, aims to con...
Premature failure of rockbolts from stress corrosion cracking (SCC) has been a problem in a limited ...