Depth-sensing indentation tests in studying plastic instabilities

This review surveys the phenomenon of plastic instabilities occurring in depth-sensing indentation measurements. Investigations presented focus on the characterization of Portevin-Le Chatelier type instabilities observed in different metal alloys during indentation. The effect of some important factors such as solute concentration, the formation of Guinier-Preston zones, and grain size and orientation are described and discussed. The phenomenon of plastic instabilities as serrated flow recently observed in bulk metallic glasses is also briefly reviewed