© Science and Education Publishing DOI:10.12691/ajmm-2-4-4 Operational Dependence of Galvanized Steel Corrosion Rate on Its Structural Weight Loss and Immersion-Point pH in Sea Water Environment

Abstract The operational dependence of galvanized steel corrosion rate on its structural weight loss and immersion-point pH (pH of stagnant sea water trapped in holes and grooves of galvanized steel made structures or equipment) in sea water environment was studied. SEM analysis of the surface structure of the corroded steel revealed that the adherent and compact nature of the white rust layers absorbed on the zinc surface affected the level of corrosion attacks on the zinc and invariably on the steel structure. The corrosion rate of the galvanized steel decreased with increase in the steel weight loss and immersion-point pH. Formation and presence of (ZnOH)2 in corrosion medium retarded the corrosion process because of its alkaline nature. A two-factorial model was derived, validated and used for the predictive evaluation of the galvanized steel corrosion rate. The validity of the model was rooted on the core model expression ζ + 5 x 10- 5 lnɤ + 6.166 x 10-5 =- 1.5 x 10- 5 ϑ2 + 0.0001ϑ where both sides of the expression are correspondingly approximately equal. The standard errors incurred in predicting the corrosion rate for each value of the weight loss & immersion-point pH considered as obtained from experiment, derived mode