STEELS By

High manganese steels offer an outstanding combination of high strength and ductility owing to their high sustained strain hardening rates. The strain-induced deformation products in these steels (mechanical twins and ε-martensite) increase the work hardening rates by acting as barriers for dislocation motion. A significant determinant of the deformation products in these steels is the value of stacking fault energy (SFE), which is in turn strongly dependent on the alloy manganese and carbon contents. The main objective of present work is to investigate the microstructural evolution and mechanical behaviour of both homogenous and compositionally graded high-Mn steels, where C compositional gradients were introduced into the latter. The starting materials in this work were cold rolled Fe-22Mn-0.6C and Fe-30Mn-0.6C steels. For both starting alloys, decarburization and annealing heat-treatments were used to obtain four homogenous alloys with carbon contents of approximately 0, 0.2, 0.4 and 0.6 wt. % with similar grain sizes. Decarburization heat treatments were also applied to obtain three carbon graded Fe-22Mn-C alloys (G1, G2, G3) and one carbon graded Fe-30Mn-C alloy. Microstructural observations determined the deformation products to b