Establishing Fracture Properties of EMC-Copper Interfaces in the Visco-Elastic Temperature Region

An ongoing root cause of failure in microelectronic industry is interface delamination. In order to explore the risk of interface damage, FE simulations for the fabrication steps as well as for the testing conditions are generally made in the design stage. In order to be able to judge the risk for interface fracture, the critical fracture properties of the interfaces being applied should be available, for the occurring combinations of temperature and moisture preconditioning. As a consequence there is an urgent need to establish these critical interface fracture parameters. For brittle interfaces such as between epoxy molding compound (EMC) and metal (-oxide) substrates the critical energy release rate (or delamination toughness) can be considered as the suitable material parameter. This material parameter is strongly dependent o