293 Microstructure and Dielectric Properties of Bi Substituted

Copyright © 2013 Hayet Menasra et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. Bismuth (Bi) and lanthanum (La) doped lead manganese antimoine zirconate titanate (PZMST) ceramic powders have been synthesized by high temperature solid-state reaction method. Preliminary X-ray structural analysis of the com-pounds shows the formation of tetragonal structure. Scanning electron micrographs (SEM) shows a uniform grain dis-tribution and grain size of the order of ~2.28 µm. Detailed dielectric studies of the Pb0.95(La1−z Biz)0.05[(Zr0.6Ti0.4)0.95(Mn1/3Sb2/3)0.05]O3 samples as a function of the temperature (from 25˚C to 450˚C) at frequency 1 kHz suggest that the compounds undergo a diffuse phase transition. The transition temperature shifts in-crease with increasing the Bi ratio. Diffusivity (γ) study of phase transition of these compounds provided its value from 1.59 to 1.78 indicating the degree of the disordering in the system