Synthesis and Characterization of Perfluorooctanoic Acid Anionic Surfactant

Surfactant doped polyaniline was synthesized in the aqueous solution of aniline and anionic sur-factant of perfluorooctanoic acid (PFO) by chemical synthesis using potassium peroxy disulphate as an oxidant by varying the aniline to surfactant ratio. The solubility of the chemically prepared surfactant doped polyaniline (PANI) was ascertained and it showed good solubility in dimethyl sulfoxide (DMSO), dimethylformamide (DMF), acetone, acetonitrile, ethanol, aceticacid, trichlo-roethylene, dichloromethane, tetrahydrofuran, ethylacetate, diethylether, toluene, chloroform and sparingly soluble in n-hexane and water. The prepared polymers were characterized by fourier transform infrared spectroscopy (FTIR), UV-visible, X-ray diffraction (XRD), cyclic voltammetric (CV), EIS and scanning electron microscopy (SEM). The analysis of UV-visible and FTIR showed that aniline has been polymerized to PANI in its conducting emeraldine form. FTIR spectra showed that the peaks at 1670, 3315 and 1400 cm−1 corresponded to PFO. FTIR spectra showed that amine peak observed at 1593 cm−1 was shifted to lower wave number due to the interaction between PANI and the surfactant. SEM analysis showed that the variation in morphology of doped PANI was predominantly dependent on the concentration of the surfactant. Elemental analysis was done b