The Effect of Phosphate Source on the Post-treatment of Cerium Based Conversion Coatings on Al 2024-T3 and its Correlation to Corrosion Performance

The surface morphology, electrochemical characteristics, and salt spray corrosion performance were studied for cerium-based conversion coatings (CeCCs) that were post-treated in heated aqueous solutions of orthophosphate, pyrophosphate, and polyphosphate compounds. Phosphate post-treatment reduced cracking in the coatings, which resulted in better corrosion protection compared to coatings that were highly cracked or contained other defects. In addition, post-treatment in orthophosphate solutions converted the as-deposited hydrated cerium oxide to hydrated CePO4, which further improved corrosion protection. Electrochemical analyses showed that CeCCs that contained hydrated CePO4 after post-treatment had the highest reVLVWDQFH a N-cm2), most noble pitting potentials ( ~-270 mV), and best corrosion protection of the post-treatments that were tested. While pyrophosphate and polyphosphate post-treatments reduced cracks in the film, they did not promote formation of CePO4Â+2O. The results suggest that the corrosion protection of CeCCs on Al 2024-T3 is dependent on both the surface morphology and phase of the coating