BEHAVIOUR OF THE EXHAUST VALVE CLADDING FACE UNDER THE SERVICE CONDITIONS

During the ship engine operation one of the key problems is the exhaust valve durability. A special interest is in valve head face because this narrow part of the valve is responsible for tightness. Cobalt base laser cladding layer on the exhaust valve head face have been investigate under real service condition using the laboratory two-stroke diesel engine L22 for two years. During this time the engine was fuelling with both ordinary light fuel and biodiesel fuel. After removing from the valve head from the cylinder head the face surface were fully inspected optically. There were no damages and the surface was shining in the great deal however some dark “spots ” on it. The samples made of the used valve head underwent microstructural investigation and hardness measurements. There were no observed substantial microstructural changes neither in the surface of the layer nor in the bulk of the clad. The decrease of the hardness numbers was observed but still clad layer presented higher hardness than steel base. This type of clad layer underwent intensive laboratory examinations which contained oxidation experiments at different temperatures and corrosion in exhaust gases and with the present service experiment this method of valve head hardfacing is suitable for practical applications