RESEARCH ARTICLE Investigation on the Tribological Behavior and Wear Mechanism of Five Different

Objectives The primary aim of this research was to investigate the wear behavior and wear mechanism of five different veneering porcelains. Methods Five kinds of veneering porcelains were selected in this research. The surface microhard-ness of all the samples was measured with a microhardness tester. Wear tests were per-formed on a ball-on-flat PLINT fretting wear machine, with lubrication of artificial saliva at 37°C. The friction coefficients were recorded by the testing system. The microstructure fea-tures, wear volume, and damage morphologies were recorded and analyzed with a confocal laser scanning microscope and a scanning electron microscope. The wear mechanism was then elucidated. Results The friction coefficients of the five veneering porcelains differ significantly. No significant corre-lation between hardness and wear volumewas found for these veneering porcelains. Under lubrication of artificial saliva, the porcelain with higher leucite crystal content exhibited greater wear resistance. Additionally, leucite crystal size and distribution in glass matrix influenced wear behavior. The wear mechanisms for these porcelains were similar: abrasive wear domi-nates the early stage, whereas delamination was the main damagemode at the later stage. Furthermore, delamination was more prominent for porcelains with larger crystal sizes. Significance Wear compatibility between porcelain and natural teeth is important for dental restorative materials. Investigation on crystal content, size, and distribution in glass matrix can provide insight for the selection of dental porcelains in clinical settings