Add to ORKGStudies were conducted to investigate the vague nature of carbon and oxygen related defects in high efficiency silicon solar cells. High temperature tests were employed to perform these investigations
This thesis work consists of two parts, each with a different motivation. Part II is the main part a...
Thesis: S.M., Massachusetts Institute of Technology, Department of Mechanical Engineering, 2017.Cata...
A summary of selected experimental results obtained on lithium-diffused bulk silicon is presented. P...
Oxygen and carbon related defects in silicon, particularly as related to high-efficiency silicon sol...
The properties of the early transistors were determined by the minority-carrier lifetime, as is the ...
Some background information on intrinsic point defects is provided and on carbon and oxygen in silic...
This report first provides some background information on intrinsic point defects, and on carbon and...
Progress reports on research in high-efficiency silicon solar cells were presented by eight contract...
Commercial silicon is prone to form silicon oxide precipitates during high-temperature treatments ty...
Oxygen and carbon are the predominant impurities in Czochralski-grown silicon. The incorporation of ...
Ce travail a pour but de comprendre les effets de deux principaux défauts liés à l’oxygène, les comp...
AbstractSingle-crystal Czochralski silicon used for photovoltaics is typically supersaturated with i...
A relationship between material defects in silicon and the performance of electronic devices will be...
The ESRF’s ID19 and BM05 beamlines have enabled scientists to watch the growth of carbon- based defe...
Cells irradiated to a fluence of 5x10,000,000,000,000/square cm showed short circuit current on anne...
This thesis work consists of two parts, each with a different motivation. Part II is the main part a...
Thesis: S.M., Massachusetts Institute of Technology, Department of Mechanical Engineering, 2017.Cata...
A summary of selected experimental results obtained on lithium-diffused bulk silicon is presented. P...
Oxygen and carbon related defects in silicon, particularly as related to high-efficiency silicon sol...
The properties of the early transistors were determined by the minority-carrier lifetime, as is the ...
Some background information on intrinsic point defects is provided and on carbon and oxygen in silic...
This report first provides some background information on intrinsic point defects, and on carbon and...
Progress reports on research in high-efficiency silicon solar cells were presented by eight contract...
Commercial silicon is prone to form silicon oxide precipitates during high-temperature treatments ty...
Oxygen and carbon are the predominant impurities in Czochralski-grown silicon. The incorporation of ...
Ce travail a pour but de comprendre les effets de deux principaux défauts liés à l’oxygène, les comp...
AbstractSingle-crystal Czochralski silicon used for photovoltaics is typically supersaturated with i...
A relationship between material defects in silicon and the performance of electronic devices will be...
The ESRF’s ID19 and BM05 beamlines have enabled scientists to watch the growth of carbon- based defe...
Cells irradiated to a fluence of 5x10,000,000,000,000/square cm showed short circuit current on anne...
This thesis work consists of two parts, each with a different motivation. Part II is the main part a...
Thesis: S.M., Massachusetts Institute of Technology, Department of Mechanical Engineering, 2017.Cata...
A summary of selected experimental results obtained on lithium-diffused bulk silicon is presented. P...