FABRICATION OF SIZE-TUNABLE NANOCRYSTALLINE COBALT PARTICLES IN PROPYLENE GLYCOL

Monodispersed and size-tunable nanocrystalline cobalt (Co) particles in the range of 100 to 400 nm are prepared by the reduction of Co(II) species in propylene glycol. Control of the particle size is achieved by varying the initial Co(II) species concentration and by the addition of nucleating agents. Smaller Co particles are produced with increasing amounts of Co(II) species and in the presence of nucleating agents. X-ray diffraction analysis (XRD) shows that the Co particles are predominantly face-centered cubic crystals of about 8-14 nm. The Co particles are also ferromagnetic at room temperature. ABSTRAK Monodispersed dan saiz boleh tala zarah-zarah nanohabluran kobalt (Co) dalam lingkungan 100 hingga 400 nm disediakan oleh pengurangan Co(II) spesies dalam propilena glikol. Kawalan saiz zarah dicapai dengan mempelbagaikan permulaan Co(II) tumpuan spesies dan oleh tambahan nucleating ejen-ejen. Zarah-zarah Co lebih kecil dikeluarkan dengan amaun-amaun yang bertambah Co(II) spesies dan dalam kehadiran nucleating ejen-ejen. Analisis pembelauan sinar-x (XRD) menunjukkan bahawa Co zarah-zarah adalah lebih banyak menghadapi tertumpu hablur-hablur padu kira-kira 8-14 nm. Zarah-zarah Co adalah juga feromagnet pada suhu bilik