Add to ORKGMagnetic nanoparticles with an average size of 11 nm have been prepared by using reverse micelle solutions. The effect of gold coating on the morphology and magnetic properties of cobalt-platinum nanoparticles were investigated by X-ray powder diffraction, energy dispersive x-ray, transmission electron microscopy and vibrating sample magnetometry. Nanoparticles that had useful magnetic properties needed to be protected from oxidation to avoid degrading the favorable magnetic properties. CoPt3 nanoparticles showed a blocking temperature of 40K and coercivity of 261.6Oe. Gold coating of CoPt3 cores with a shell thickness of 5nm further enhanced blocking temperature and coercivity to 45K and 421.1Oe respectively
High magnetocrystalline anisotropy CoPt particles with an average size of 8 nm were synthesized by t...
Abstract The superparamagnetic (SPM) cobalt nano-particles with an average size of 2 nm have been pr...
The magnetic response of nanometer sized Co nanoparticles (NP) prepared using reverse micelle solut...
Magnetic nanoparticles with an average size of 11 nm have been prepared by using reverse micelle sol...
Cobalt nanoparticles and cobalt-gold core-shell nanoparticles were synthesized via reverse-micelle m...
This thesis is focused on the preparation of cobalt and cobalt-platinum type magnetic nanoparticles ...
Size-controlled cobalt–gold core–shell nanoparticles were synthesized via the reverse-micelle microe...
Size-controlled cobalt–gold core–shell nanoparticles were synthesized via the reverse-micelle microe...
In this work we present the study on structural and magnetic properties of fine cobalt nanoparticles...
A comparative experimental study of the magnetic properties of CoPt3 and CoPt3/Au nanoparticles as w...
We present for the first time a nonaqueous sol-gel route to produce ultrasmall (<2 nm) magnetic b...
We present for the first time a nonaqueous sol-gel route to produce ultrasmall (<2 nm) magnetic b...
Using microemulsion methods, CoO-Pt core-shell nanoparticles, with diameters of nominally 4 nm, were...
Nanosized iron-gold magnetic nanoparticles with an average particle size 10 nm were prepared by a re...
In this work, the structural and magnetic properties of the gold- coated FePt nanoparticles synthesi...
High magnetocrystalline anisotropy CoPt particles with an average size of 8 nm were synthesized by t...
Abstract The superparamagnetic (SPM) cobalt nano-particles with an average size of 2 nm have been pr...
The magnetic response of nanometer sized Co nanoparticles (NP) prepared using reverse micelle solut...
Magnetic nanoparticles with an average size of 11 nm have been prepared by using reverse micelle sol...
Cobalt nanoparticles and cobalt-gold core-shell nanoparticles were synthesized via reverse-micelle m...
This thesis is focused on the preparation of cobalt and cobalt-platinum type magnetic nanoparticles ...
Size-controlled cobalt–gold core–shell nanoparticles were synthesized via the reverse-micelle microe...
Size-controlled cobalt–gold core–shell nanoparticles were synthesized via the reverse-micelle microe...
In this work we present the study on structural and magnetic properties of fine cobalt nanoparticles...
A comparative experimental study of the magnetic properties of CoPt3 and CoPt3/Au nanoparticles as w...
We present for the first time a nonaqueous sol-gel route to produce ultrasmall (<2 nm) magnetic b...
We present for the first time a nonaqueous sol-gel route to produce ultrasmall (<2 nm) magnetic b...
Using microemulsion methods, CoO-Pt core-shell nanoparticles, with diameters of nominally 4 nm, were...
Nanosized iron-gold magnetic nanoparticles with an average particle size 10 nm were prepared by a re...
In this work, the structural and magnetic properties of the gold- coated FePt nanoparticles synthesi...
High magnetocrystalline anisotropy CoPt particles with an average size of 8 nm were synthesized by t...
Abstract The superparamagnetic (SPM) cobalt nano-particles with an average size of 2 nm have been pr...
The magnetic response of nanometer sized Co nanoparticles (NP) prepared using reverse micelle solut...