l Resistance Spot Welding of Galvanized Steel: Part I. Material Variations and Process Modifications

Material variations and process modifications have been studied to determine their effects on the acceptable range of resistance spot welding conditions for galvanized steel sheet. The material variations studied include zinc coating integrity, structure, composition, thickness, roughness, oil, and the amount and type of Fe-Zn intermetallics. Process modifications studied include upsloping and downsloping of the weld current, preheat current, postheat current, electrode tip geometry, and applied force. It was found that hot-dipped galvanized materials with coatings which have a very thin Fe-Zn alloy layer have a wider range of acceptable welding conditions than the commercial galvannealed products, which have a fully alloyed Fe-Zn coating. The decreased lobe width of the galvannealed material is due to the discontinuous Fe-Zn coating structure and morphology. Small variations in the thickness of the coatings studied have no significant effect on the welding current range. Surface roughness of the coating has no effect on lobe width. Ups loping and downs loping of the weld current increase the welding range of hot-dipped products when using truncated cone electrodes, whereas sloped current has no advantage for galvannealed or uncoated materials. Radiused electrodes can increase the lobe width of hot-dipped products but are not beneficial when using sloped currel)t or when welding galvannealed or uncoated materials. I