Effect of Spark Plasma Sintering in Fabricating Carbon Nanotube Reinforced Aluminum Matrix Composite Materials

Carbon nanotubes (CNT) are attractive next generation materials due to their unique properties, which lead to high mechanical, electrical, and thermal performance (Iijima, 1991; Endo et al., 1976; Niyogi et al., 2002; Komarov & Mirnov, 2004). This unique nano order material can not only be utilized on its own in precision industrial fields but can also provide high performance functionality in conjunction with conventional materials. For this reason, many researchers are investigating the fabrication of CNT reinforced metal, ceramic, and polymer matrix composite materials. Despite their research efforts, the fabrication of CNT-reinforced metal matrix composite materials, particularly with an aluminum (Al) matrix, is still facing several problems, such as difficulties in homogeneously dispersing the CNT in the Al matrix, (Salvetat-Delmotte and Rubio, 2002; Hilding et al., 2003; Xu et al., 1999) producing highly densified composite materials without any degradation of the CNT, (Kuzumaki et al., 1998; Sridhar & Narayana, 2009) and achieving enough interface strength between the Al matrix and reinforcement of CNT (Deng et al., 2007; Bakshi et al., 2009; Lahiri et al., 2009). To overcome these problems, Deng et al. fabricated the CNT-Al alloy composite materials by cold isostatic pressing and then subsequent hot extrusio