Add to ORKGTheinfluenceofshotpeeningovercorrosion,stresscorrosion,corrosionfatigueand fracture behaviour of carbon steel has been studied. A laboratory equipment for stresscorrossiontesting wasdesignedandfabricated(vertica1type). Further, it was modified into 'horizontal type'foreasierloading and unloading of the test specimen. Test specimens were peened manually. The controlled peening showed that there was reduction in loss of weight, improvement in stress corrosion resistance and corrosion fatigue resistance when combined with carburising treatment. Shot peening alone did not show any appreciable improvement in corrosion fatigue resistance. It wasalsoobservedthatshot peeningdelayed rateof crackpropagation for notched specimens
Rotary bending fatigue tests were performed on annealed and shot-peened specimens in laboratory air ...
Notched specimens with a stress concentration factor common in many structural components have been ...
One of the traditional methods used to improve the fatigue properties of metallic materials is shot ...
In this present study, the effect of the shot peening process on fatigue life, surface hardness and ...
Used with the right combination of parameters, shot peening process can be regarded as a severe plas...
Corrosion fatigue is a common failure mechanism in rock drilling components and many othermechanical...
Stress corrosion cracking(SCC) is a progressive fracture mechanism in metals that is caused by the s...
Corrosion can deteriorate the material as a result of reaction with its environment. It is one of th...
AbstractA quenched and tempered medium-carbon alloyed steel was subjected to different shot peening ...
Ferritic stainless steels are used in specific applications where corrosion resistance, oxidation re...
In landing gear, an important mechanical component for high responsible applications, wear and corro...
Pitting corrosion was observed in welded carbon steel tanks which had been stress relieved to improv...
Proceedings of ICSB1. Editor: A. Niku-Lari, X-ray diflractometry has been used to examine the variat...
The influence of shot peening on high cycle fatigue behaviour of spring steel was investi-gated. The...
Shot peening is used in many industrial applications, e.g. steam turbine blades, to induce near-surf...
Rotary bending fatigue tests were performed on annealed and shot-peened specimens in laboratory air ...
Notched specimens with a stress concentration factor common in many structural components have been ...
One of the traditional methods used to improve the fatigue properties of metallic materials is shot ...
In this present study, the effect of the shot peening process on fatigue life, surface hardness and ...
Used with the right combination of parameters, shot peening process can be regarded as a severe plas...
Corrosion fatigue is a common failure mechanism in rock drilling components and many othermechanical...
Stress corrosion cracking(SCC) is a progressive fracture mechanism in metals that is caused by the s...
Corrosion can deteriorate the material as a result of reaction with its environment. It is one of th...
AbstractA quenched and tempered medium-carbon alloyed steel was subjected to different shot peening ...
Ferritic stainless steels are used in specific applications where corrosion resistance, oxidation re...
In landing gear, an important mechanical component for high responsible applications, wear and corro...
Pitting corrosion was observed in welded carbon steel tanks which had been stress relieved to improv...
Proceedings of ICSB1. Editor: A. Niku-Lari, X-ray diflractometry has been used to examine the variat...
The influence of shot peening on high cycle fatigue behaviour of spring steel was investi-gated. The...
Shot peening is used in many industrial applications, e.g. steam turbine blades, to induce near-surf...
Rotary bending fatigue tests were performed on annealed and shot-peened specimens in laboratory air ...
Notched specimens with a stress concentration factor common in many structural components have been ...
One of the traditional methods used to improve the fatigue properties of metallic materials is shot ...