ANALYSIS OF LOW CYCLE FATIGUE IN AlMgSi ALUMINIUM ALLOYS

Abstract. In this study low cycle fatigue tests were performed in two AlMgSi aluminium alloys with different chemical composition, namely 6082-T6 and 6060-T6 alloys, using standard round specimens and tube specimens, respectively. The tests were undertaken in strain control with a strain ratio Re=–1. The cyclic stress-strain curves were determined using one specimen for each imposed strain level. The low cycle fatigue results are used for the characterisation of the cyclic plastic response and the fatigue live of the alloys. Moreover, the geometry of the hysteresis loops and the occurrence of Masing behaviour are also analysed. The observed behaviour is discussed in terms of the chemical composition of the alloys (Mg2Si hardening particles and Mn dispersoid content) and fracture mechanisms. Alloy 6060-T6 exhibits nearly ideal Masing behaviour, while alloy 6082-T6 presents significant deviations from Masing model. The type of cyclic deformation behaviour in AlMgSi alloys seems to be influenced by the dispersoid phase. Resumo. Neste estudo foram realizados ensaios de fadiga oligocíclica em duas ligas de alumínio AlMgSi com diferente composição química, nomeadamente ligas 6082-T6 e 6060-T6, utilizando provetes cilíndricos normalizados e provetes em tubo, respectivamente. Os ensaios foram executados em controlo de deformação com uma razão de extensão Re=–1. As curvas cíclicas tensão-deformação foram determinadas utilizando o método de um provete por cada nível de extensão imposta. Os resultados de fadiga oligocíclica são usados para caracterizar a resposta em termos da deformação plástica cíclica e da vida de fadiga das ligas. Adicionalmente é analisada a geometria dos circuitos de histerese e