Laser-driven synthesis and magnetic properties of iron nanoparticles

Nanoparticles of iron have been prepared by laser-driven decomposition of iron pentacarbonyl vapor. In this method, an infrared laser rapidly heats a dilute mixture of precursor vapors to decompose the pre-cursor and initiate particle nucleation. It was found that when using SF6 as a photosensitizer during the synthesis, ferrous fluoride (FeF2) was produced as an undesired byproduct in the product powder. The particle size, composition, and crystalline structure have been characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), selected area electron diffraction (SAED), and X-ray photo-electron spectroscopy (XPS). Results of magnetization measurements for small iron nanoparticles (about 5 nm diameter) are also presented, showing superparamagnetic behavior at room temperature, and a blocking temperature near 125 K