Preparation and electrochemical study of cerium–silica sol–gel thin films

Design and development of suitable multilayered systems for delaying corrosion advance in metals requires that both the alteration mechanisms of the metal and the behaviour and properties of the protective coatings be known. Coatings prepared by the sol–gel method provide a good approach as protective layers on metallic surfaces. This kind of coatings can be prepared from pure chemical reagents at room temperature and atmospheric pressure, with compositions in a very wide range of environmentally non-aggressive precursors. Sol–gel coatings based on siloxane bonded units were prepared starting from an organic–inorganic hybrid system. The precursors were -methacryloxypropyltrimethoxysilane (MAP) and tetramethoxysilane (TMOS). Cerium nitrate hexahydrate in three different concentrations was added. Cerium salts may perform a similar protective effect to that carried out by the well-known lead oxides and chromium salts, even though in this case a negative environmental impact is not expected. Application of coatings upon pure zinc substrates and common glass slides were performed by spinning. Coated samples were heat treated at 40 ◦C for 6 days. Optical measurements (UV-Vis absorption and diffuse reflectance spectroscopies) pointed out that the coatings were colourless and transparent, reducing the diffuse reflectance of the metallic surface up to ∼60%. Optical and scanning electron microscopies (SEM) allowed observation of the texture and microstructure of the coated samples, both before and after the corrosion tests were carried out. Likewise, the remaining sols were kept to gelify at 60 ◦C for 4 days and then powdered to obtain suitable samples for analysing them by other characterisation techniques (Fourier transformed infrared, FTIR and differential thermal analysis, DTA). Electrochemical measurements were performed by impedance spectroscopy. This technique was used t