2 Nanostructured and Eco-efficient Materials for Construction Unit,

This study forms part of wider research conducted under a EU 7th Framework Programme (COmputationally Driven design of Innovative CEment-based materials or CODICE). The ultimate aim is the multi-scale modelling of the variations in mechanical performance in degraded and non-degraded cementitious matrices. The model is being experimentally validated by hydrating the main tri-calcium silicate (T1-C3S) and bi-calcium silicate (β-C2S), phases present in Portland cement and their blends. The present paper discusses micro- and nanoscale studies of the cementitious skeletons forming during the hydration of C3S, C2S and 70 % / 30 % blends of both C3S/C2S and C2S/C3S with a water/cement ratio of 0.4. The hydrated pastes were characterized at different curing ages with 29Si NMR, SEM/TEM/EDS, BET, and nanoindentation. The findings served as a basis for the micro- and nanoscale characterization of the hydration products formed, especially C-S-H gels. Differences were identified in composition, structure and mechanical behaviour (nanoindentation), depending on whether the gels formed in C3S or C2S pastes. The C3S gels had more compact morphologies, smaller BET-N2 specific surface area and lesser porosity than the gels from C2S-rich pastes. The results of nanoindentation tests appear to indicate that the various C-S-H phases formed in hydrated C3S and C2S have the same mechanical properties as those formed in Portland cement paste. Compared to the C3S sample, the hydrated C2