Controlling interchain interactions in conjugated polymers: The effects of chain morphology on exciton-exciton annihilation and aggregation in meh-ppv films

The presence of interchain species in the photophysics of conjugated polymer films has been the subject of a great deal of controversy. In this paper, we present strong evidence that interchain species do form in conjugated polymer films, and that the degree of interchain interactions can be controlled by varying the solvent and polymer concentration of the solution from which the films are cast. Thus, much of the controversy in the literature can be resolved by noting that the polymer samples in different studies had different side groups or were prepared in different ways and thus have different degrees of interchain interaction. The photoluminescence (PL) of poly(2-methoxy-5-(2′-ethylhexyloxy)-1,4-phenylene vinylene), MEH-PPV, changes both its spectral shape and quantum yield when the films are prepared from different solutions or when the morphology is varied by annealing. Increasing the amount of interchain interactions enhances the red portion of the film’s PL, a result assigned to a combination of changes in the vibronic structure of the PL of the exciton and increased numbers of weakly emissive interchain species. Photoluminescence excitation spectroscopy shows that excitation to the red edge of the absorption band preferentially enhances the red emission, suggesting that the interchain species are aggregates with a distinct ground state absorption. Scanning force microscopy shows topographic features that correlate with the degree of interchain interactions, verifying that the morphology of conjugated polymer films changes with polymer concentration, choice of solvent, an