Thick

This Thesis explores the deposition techniques of magnetron sputtering and high velocity oxy-fuel (HVOF) spraying for Ti2AlC as a promising high-temperature material. Magnetron sputtering aims at producing thin (≤1 µm) Ti2AlC films of high crystal quality for use as a model system in understanding the material’s basic properties. HVOF is a new method for deposition of thick (≥200 µm) coatings by spraying Ti2AlC powder, with the aim of transferring the good bulk properties to coatings. The oxidation behavior of Ti2AlC coatings has been investigated for temperatures up to 1200 °C in air. As-deposited Ti2AlC(0001) thin films decompose into TiC during vacuum annealing at 700 °C by out-diffusion of Al as shown by x-ray diffraction analysis. The release of Al starts already at 500 °C in ambient air as driven by aluminum oxide formation on the film surface where the oxide initially forms clusters as observed by electron microscopy. While sputtering from a Ti2AlC target is simpler than by using different elemental targets, the resulting film composition differs from the target stoichiometry. This is due to differences in energy and angular distribution of the sputtered species and evaporation of Al at substrate temperatures above 700 °C. The composition can b