Fabrication of Conjugated Polymer Nanowires by Edge Lithography

This paper describes the fabrication of conjugated polymer nanowires by a three stage process: (i) spin-coating a composite film comprising alternating layers of a conjugated polymer and a sacrificial material, (ii) embedding the film in an epoxy matrix and sectioning it with an ultramicrotome (nanoskiving), and (iii) etching the sacrificial material to reveal nanowires of the conjugated polymer. A free-standing, 100-layer film of two conjugated polymers was spin-coated from orthogonal solvents: poly(2-methoxy-5-(2′-ethylhexyloxy)-1,4-phenylenevinylene) (MEH-PPV) from chloroform and poly(benzimidazobenzophenanthroline ladder) (BBL) from methanesulfonic acid. After sectioning the multilayer film, dissolution of the BBL with methanesulfonic acid yielded uniaxially aligned MEH-PPV nanowires with rectangular cross sections, and etching MEH-PPV with an oxygen plasma yielded BBL nanowires. The conductivity of MEH-PPV nanowires changed rapidly and reversibly by>103 upon exposure to I2 vapor. The result suggests that this technique could be used to fabricate high-surface-area structures of conducting organic nanowires for possible applications in sensing and in other fields where a high surface area in a small volume is desirable. We have developed a method for the fabrication of electri-callyconductivenanowiresoftwoconjugatedpolymersspoly(2-methoxy-5-(2′-ethylhexyloxy)-1,4-phenylenevinylene) (MEH-PPV) and poly(benzimidazobenzophenanthroline ladder) (BBL)sby sectioning spin-coated multilayer films with an ultramicrotome (“nanoskiving”, see Figure 1 for chemica